Download the 3M AC-130-2 technical data sheet (TDS) and the 3M AC-130-2 safety data sheet (SDS) from Silmid today. Once you have logged in or signed up, select the product size you are interested in and the datasheet will be visible for download if one is available.Please login and select size/colour from the dropdown to access datasheets

Product Properties

Brand

3M

Manufacturer Part Number

7000048286 | 7000048290 | 7000048292

Specifications

Boeing

BMS 5-162 Type 1 Form 2S | BMS 10-128 Type I Class A Grade A

Please Note: Specifications and approvals are subject to change at any time. Users should always consult their AMM or the OEM when selecting products to ensure items have the release needed. Only specifications listed on the order confirmation will be certified on the Silmid CofC.

Product Information

3M Surface Pre-Treatment AC-130-2 is a high-performance surface preparation for adhesive bonding of aluminum alloys, steel and titanium. AC-130-2 may address concerns about economical and environmental issues found in other conventional processes.Water-based and non-chromated,

3M AC-130-2 may help reduce the amount of hazardous materials and waste typically generated by the bonding surface preparation process. It is also faster and easier to apply, even in the field

Features:

Helps improve process efficiency

Up to 35% reduction in labour times

Helps minimize aircraft on ground

Two part surface pre treatment

The most common surface preparation techniques used to provide acceptable surfaces for bonding (i.e., phosphoric acid anodizing or sulfuric acid-sodium dichromate etchings) generate hazardous materials and waste that require special handling, control and disposal methods.

When used with the leading adhesive primers and adhesives, 3M AC-130-2 provides an economical alternative to these more costly processes. Testing of 3M AC-130-2 coated surfaces has demonstrated the long-term durability of adhesion to metal. In addition, test data shows that AC-130-2 provides equivalent or better moisture durability than many of the currently used surface preparations for on-aircraft repairs